| TYPICAL PHYSICAL PROPERTIES | % |
| % Solids | 60.0-61.0 |
| Specific Gravity | 1.585-1.600 |
| Dry MOR (psi) =50% Clay/50% Flint | 715 |
| Linear Dryng Shrinkage (%)-100% Clay | 6.3 |
| Soluble Sulfates (ppm) | 300-450 |
| CEC/MBI (meq/100 ml) | 9.3 |
| Specific Surgace Area (m2/g) | 17.2 |
| pH@90 F (cps) | 5.0 |
| Viscosity* @ 90 F (cps) | 100-300 |
| Drop On Curve* @ 90 F (cps) | 40-100 |
| Deflocculant Type | Sodium Silicate [N Brand] |
| Particle Size Distribution (% finer than) 5 Microns 1 Micron .5 Microns |
77 52 43 |
| Median Particle Diameter (um) | 0.87 |
| TYPICAL CHEMICAL ANALYSIS | % |
| Silicon Dioxide (SiO2) | 56.4 |
| Aluminum Oxide (Al2O3) | 28.0 |
| Iron (Ferric) Oxide (Fe2O3) | 1.5 |
| Titanium Dioxide (TiO2) | 1.7 |
| Calcium Oxide (CaO) | 0.2 |
| Magnesium Oxide (MgO) | 0.4 |
| Sodium Oxide (Na2O) | 0.1 |
| Potassium Oxide (K2O) | 1.4 |
| Loss on Ignition | 10.4 |
. 